Rigidex® HD6070FA

Category:	HDPE , High Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Rigidex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kxX8hH_Rigidex-HD6070FA.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Rigidex® HD6070FA is a high density polyethylene suitable for a range of high quality film applications.

Typical applications

Cast or blown film as a blending partner to increase stiffness of LDPE or LLDPE

Cast co-extrusion for high stiffness films or non blocking layers

Extrusion coating as a blending partner or in co-extrusion with LDPE extrusion coating grades. With such blends (minimum content of LDPE of 20%), coated substances such as paper and cardboard can be used e.g. for photographic paper and for ream wrapping.

Benefits and Features

High stiffness

Very low gel level

Easy extrudability

Good optical properties in cast extrusion

High gloss

Better heat and scratch resistance compared to LDPE and lower blocking

In extrusion coating : good processability, high coating speed, good draw down ability with reasonable neck-in, good adhesion on many substrates

General Information
Additive	Antioxidant
Features	Antioxidant Good Adhesion Good Drawdown Good Processability High Density High Gloss High Stiffness Low Gel Opticals
Uses	Blending Blown Film Cast Film Coating Applications Film Paper Coatings
RoHS Compliance	Contact Manufacturer
Forms	Pellets
Processing Method	Blown Film Cast Film Coextrusion Extrusion Coating

Physical	Nominal Value	Unit	Test Method
Density	0.960	g/cm³	ISO 1872
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	7.6	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Tensile Modulus - 1% Secant (15 µm, Cast Film)	700	MPa	ISO 1184
Tensile Stress (Break, 15 µm, Cast Film)	50.0	MPa	ISO 1184
Tensile Elongation (Break, 15 µm, Cast Film)	500	%	ISO 1184

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	127	°C	ISO 306/A
Melting Temperature (DSC) ¹	132	°C	Internal Method
Specific Heat	2300	J/kg/°C
Thermal Conductivity	0.48	W/m/K	ASTM C177

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 15.0 µm, Cast Film)	75		ASTM D2457
Haze (15.0 µm, Cast Film)	7.0	%	ASTM D1003

Note Message
1 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
BRALEN® FB 3-33	Slovnaft Petrochemicals, s.r.o.	LDPE	BRALEN®
INEOS PP 200-CA25	INEOS Olefins & Polymers Europe	PP Random Copolymer	INEOS PP
Interpol 47-5138/47-5205	Cook Composites and Polymers	PUR-Ester	Interpol
LNP™ LUBRICOMP™ FX86496 compound	SABIC Innovative Plastics	PE, Unspecified	LNP™ LUBRICOMP™
LNP™ THERMOCOMP™ EF006H compound	SABIC Innovative Plastics	PEI	LNP™ THERMOCOMP™