PELPRENE™ S9002 is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.8 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.28 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A | 99 | JIS K6301 | |
| Shore D | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 52.0 | MPa | |
| 50% Strain | 44.1 | MPa | |
| Tensile Elongation (Break) | 380 | % | ASTM D638 |
| Flexural Modulus | 911 | MPa | ASTM D790 |
| Compressive Strength (10% Strain) | 39.2 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 6.00 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 250 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 146 | °C | ASTM D648 |
| Brittleness Temperature | -50.0 | °C | JIS K6301 |
| Vicat Softening Temperature | 207 | °C | ASTM D1525 |
| Melting Temperature | 223 | °C | DSC |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | JIS K2111 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Random Copolymer RP200 | M. Holland Company | PP Random Copolymer | MTEGRITY™ PP Random Copolymer |
| ULTEM™ 1000RV resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| KEBATER® PBT A1100 | BARLOG plastics GmbH | PC+PBT | KEBATER® |
| Sinpolene MFP24ZA4 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | SINPOLENE |
| ESTOPLAST XU 400NN12 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |