LNP™ STAT-KON™ FX91304 compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kv3DCV_LNP-STAT-KON-FX91304-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON FX91304 is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-F-91304 Product reorder name: FX91304 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 0.940 | g/cm³ | |
| -- | 0.948 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.70 | % | |
| Across Flow : 24 hr | 0.20 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.012 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3000 | MPa | ASTM D638 |
| -- | 2430 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 27.2 | MPa | ASTM D638 |
| Yield | 26.1 | MPa | ISO 527-2/5 |
| Break 3 | 24.6 | MPa | ASTM D638 |
| Break | 22.1 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2/5 |
| Break 5 | 3.7 | % | ASTM D638 |
| Break | 3.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1800 | MPa | ASTM D790 |
| -- 7 | 2120 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 36.7 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 35.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 9 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 510 | J/m | ASTM D4812 |
| 23°C 10 | 31 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.0 | J | ASTM D3763 |
| -- | 4.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 97.4 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 72.3 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 67.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 2.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 6.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 195 to 205 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 230 | °C | |
| Mold Temperature | 40.0 to 55.0 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 4571 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| RTP ESD A 2800-50D | RTP Company | TPO (POE) | RTP |
| Network Polymers PP PPB 25 0202 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Network Polymers LDPE 10 1010 EVA | Network Polymers, Inc. | EVA | Network Polymers LDPE |
| Adflex KS311P | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |