Borealis PE FT5230
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kuF05W_Borealis-PE-FT5230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FT5230 is a Low Density Polyethylene for Film Extrusion. Tubular Technology. Unmodified. This grade is developed for the production of packaging film with good optical properties for medium duty film applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.80 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Puncture Energy (40 µm) | 2.50 | J | ASTM D5748 |
| Film Puncture Force (40 µm) | 66.0 | N | ASTM D5748 |
| secant modulus | ASTM D882A | ||
| MD : 40 µm | 230 | MPa | ASTM D882A |
| TD : 40 µm | 260 | MPa | ASTM D882A |
| Tensile Strength | ISO 527-3 | ||
| MD : 40 µm | 27.0 | MPa | ISO 527-3 |
| TD : 40 µm | 24.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 250 | % | ISO 527-3 |
| TD : Break, 40 µm | 550 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm | 4.0 | N | ISO 6383-2 |
| TD : 40 µm | 2.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 112 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm) | 85 | ASTM D2457 | |
| Haze (40.0 µm) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Extrusion instructions |
|---|
| Draw Down: 25 to 30µ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600-PA66-GV 25 HWV0CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| SABIC® PPcompound 2609B | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| DEXFLEX® 815 BLK XXX | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| LEXAN™ 123 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LEXAN™ 500R resin | SABIC Innovative Plastics | PC | LEXAN™ |