ASTALON™ E2000U
| Category: | PC , Polycarbonate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kuB1Vg_ASTALON-E2000U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALON™ E2000U / E2001U / E2003U are the high viscosity (low melt flow) grades in the ASTALON™ range and are well suited to extrusion sheeting, rod and profile applications requiring UV stabilisation (U). Offering an excellent balance of transparency, toughness, UV stability, flame retardancy and processability, typical applications include fluorescent lamp tubes, telephone box enclosures, corrugated roof sheeting and shutter door panels. Note: [ Standard grade = E2000U ] / [ FDA approved = E2001U ] / [ Steam resistant = E2003U ]. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 120 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 1000 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | > 85.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 153 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 138 | °C | |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.1E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant | 2.85 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total, 3000 µm) | 85.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 125 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Cylinder Zone 1 Temp. | 230 to 250 | °C | |
| Cylinder Zone 2 Temp. | 235 to 260 | °C | |
| Cylinder Zone 3 Temp. | 240 to 265 | °C | |
| Cylinder Zone 4 Temp. | 245 to 270 | °C | |
| Cylinder Zone 5 Temp. | 250 to 280 | °C | |
| Melt Temperature | 250 to 290 | °C | |
| Die Temperature | 240 to 280 | °C | |
| Take-Off Roll | 80.0 to 130 | °C | |
| Back Pressure | 10.0 to 25.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Polyester 85-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| TECHLEN H7348 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| 4PROP® 9C12450 | 4Plas | PP Copolymer | 4PROP® |
| Nypol® PA A3 T25 FR CNZ0093 NR328 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Gallonprene® GP200-16 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |