Clyrell RC449S
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Clyrell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ksx4NH_ClyrellRC449S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clyrell RC449S is a development polypropylene resin with nucleation and antistatic additivation designed for injection molding. It features an excellent combination of outstanding transparency and a good stiffness-impact balance that enables customers to achieve excellent organoleptic performance and a superior aesthetic appearance which appeals to end users. The product contains the most advanced clarifier system that allows easy processing at significantly lower temperatures than similar resins, which customers report enables them to reduce cycle times to save energy and improve productivity. It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 42 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1250 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 12 | % | ISO 527-2/50 |
| Fracture, 23°C | > 50 | % | ISO 527-2/50 |
| Flexural Modulus - Secant 1(23°C) | 1220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| 0°C | 1.5 | kJ/m² | ISO 179 |
| 23°C | 4.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 75.0 | °C | ISO 75-2/B |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 137 | ASTM D2457 | |
| Haze (1000 µm) | 6.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 620TIC | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| Taitalac® 1003 | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| Witcom PA66 1L2 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Hostacom M4 W01 100000 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Hifax TRC 277P S71487 | LyondellBasell Industries | PP Copolymer | Hifax |