LNP LUBRICOMP CX05031 is a compound based on Polystyrene resin containing Graphite, Silicone. Added features include; Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound CL-4350 S Product reorder name: CX05031 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6900 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 30.0 | MPa | |
| Break | 24.0 | MPa | |
| Tensile Strain (Yield) | 0.60 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6400 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 48.0 | MPa | |
| -- 4 | 51.0 | MPa | |
| Flexural Strain at Break 5 | 2.4 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 5.0 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 87.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 81.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Break |
| 4 . | Yield |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA1212 GYBLVN | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Aurora PVC AP2144 Series 032405 | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| ChronoThane™ T 80A | AdvanSource Biomaterials Corp. | TPU-Polyether | ChronoThane™ |
| ELASTOSIL® LR 3071/60 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| SQUARE® LIM3900-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |