RTP 107 CC UV
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ksAAWX_RTP-107-CC-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - Chemically Coupled - UV Stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8960 | MPa | ASTM D638 |
| Tensile Strength | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 157 | °C | |
| 1.8 MPa, Unannealed | 141 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P30N11 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| VINIKA® D2047E | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| ExxonMobil™ PP1105E1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Formolene® L63568U | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| SQUARE® LIM1530-35A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |