NYCOA Polyamide 2237
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | krcMEn_NYCOA-Polyamide-2237.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2237 is Nylon copolymer resin that exhibits excellent transparency and good barrier properties. The resin was developed especially for applications requiring transparency in thickness up to 5 mm, while retaining the properties and chemical resistanc NYCOA 2237 has been specifically designed to offer easy processability. It can be processed on conventional extrusion and injection equipment designed to process standard grades of nylon. NYCOA 2237 is available with custom additive packages: heat stabilizer and/or UV stabilizer. Typical injection molding applications include sight glasses, chemical splash goggles, fashion eyeglass frame, high-voltage switch casings, filter housings, pump casings, flow meters, liquid-level indicators, and filter bowls for gas. Typical extrusion applications include high-end transparent fishing lines, tubing, transparent sheets, and decorative films for sports and automotive applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 | % | ASTM D955 |
| Transverse flow | 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 75.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 100 | % | ASTM D638 |
| Flexural Modulus 3 | 2200 | MPa | ASTM D790 |
| Flexural Strength 4 | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 199 | °C |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 204 - 216 | °C | |
| Middle Temperature | 216 - 227 | °C | |
| Front Temperature | 221 - 232 | °C | |
| Nozzle Temperature | 221 - 238 | °C | |
| Processing (Melt) Temp | 216 - 232 | °C | |
| Mold Temperature | 4.44 - 10.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResinDirect RCOPP35 | ResinDirect | PP Random Copolymer | ResinDirect |
| Flontech® FT-GL25-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| KW Plastics KWR102-8812 BLK | KW Plastics | HDPE | KW Plastics |
| RONFALIN® ABS 1411 GF 30 | A. Schulman Europe | ABS | RONFALIN® |
| NORYL GTX™ GTX975 resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |