NORYL PPX™ PPX630 resin
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL PPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kpsPRg_NORYLPPXPPX630resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 2.6 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.20 - 0.23 | % | Internal method |
| Transverse flow : 3.20mm | 0.25 - 0.76 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 79.3 | MPa | ASTM D638 |
| Fracture | 79.3 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 7.7 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 5560 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 170 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 830 | J/m | ASTM D4812 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 20.4 | J | ASTM D3763 |
| 23°C, Total Energy | 19.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 155 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 134 | °C | ASTM D648 |
| Vicat Softening Temperature | 162 | °C | ASTM D1525 5 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.7E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 76.7 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 243 - 288 | °C | |
| Middle Temperature | 249 - 288 | °C | |
| Front Temperature | 254 - 293 | °C | |
| Nozzle Temperature | 260 - 299 | °C | |
| Processing (Melt) Temp | 260 - 299 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.051 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecopet® PT70 GR30 NL100 PS20 | Eurotec Engineering Plastics | PET | Tecopet® |
| Sorona® 3301V BK001 | DuPont Performance Polymers | PTT | Sorona® |
| Victron® 095G4 | Asia International Enterprise (Hong Kong) Limited | PEEK | Victron® |
| Chansieh Phenolic J-160P | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| ULTEM™ ATX200 resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |