HiFill® PEEK GF40 A HF
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kpDISl_HiFill-PEEK-GF40-A-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PEEK GF40 A HF is a Polyetheretherketone (PEEK) product filled with glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 207 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 13800 | MPa | ASTM D790 |
| Flexural Strength | 303 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 325 | °C | ASTM D648 |
| Melting Temperature | 342 | °C | |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 249 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 360 to 388 | °C | |
| Middle Temperature | 360 to 388 | °C | |
| Front Temperature | 360 to 388 | °C | |
| Processing (Melt) Temp | 360 to 382 | °C | |
| Mold Temperature | 177 to 218 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SANTAC® UT-61 | Nippon A&L Inc. | ABS | SANTAC® |
| Nypol® PA A2 VRM0004 NR232 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Cawiton® MT950 | Wittenburg B.V. | SEBS | Cawiton® |
| Edgetek™ RA-10GF-10CF/000 HI | PolyOne Corporation | PPSU | Edgetek™ |
| Domamid HT™ 7750R30H3 | Technical Polymers, LLC | Nylon 66 | Domamid HT™ |