Akulon® S223-HG0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kmlyXO_AkulonS223HG0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon®S223-HG0 is a polyamide 66 (nylon 66) material, which contains a 50% glass fiber reinforced material. This product is available in North America or Asia Pacific,. Akulon®The main features of the S223-HG0 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.2 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16800 | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 245 | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.6 | 6.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 14 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 16 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 97 | 68 | kJ/m² | ISO 179/1eU |
| 23°C | 90 | 88 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 253 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (1.6 mm) | HB | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 275 - 295 | °C | |
| Middle Temperature | 275 - 295 | °C | |
| Front Temperature | 275 - 290 | °C | |
| Nozzle Temperature | 280 - 290 | °C | |
| Processing (Melt) Temp | 290 - 305 | °C | |
| Mold Temperature | 50 - 80 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4278 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RX® 431 | Sumitomo Bakelite North America, Inc. | Phenolic | RX® |
| TAIRILAC AG12A3 | Formosa Plastics Corporation | ABS | TAIRILAC |
| TAROLOX 111 G4 DX0 | Taro Plast S.p.A. | PET | TAROLOX |
| Plenco 02311 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |