Adell Polyamide AF-10-667B
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kltgrS_Adell-Polyamide-AF-10-667B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Adell Polyamide AF-10-667B is a Polyamide 66 (Nylon 66) material. It is available in North America. Primary attribute of Adell Polyamide AF-10-667B: Flame Retardant. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 27 | J/m | ASTM D256 |
| Tensile Impact Strength | 73.6 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 232 | °C | |
| 1.8 MPa, Unannealed | 149 | °C | |
| Melting Temperature | 249 to 260 | °C | |
| RTI Elec (0.710 mm) | 130 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.710 mm | 75.0 | °C | |
| 1.47 mm | 80.0 | °C | |
| RTI Str | UL 746 | ||
| 0.710 mm | 120 | °C | |
| 1.47 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance (3.05 mm) | 60.0 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) (3.05 mm) | 138 | V | UL 746 |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.710 mm | 45.0 | ||
| 3.05 mm | 90.0 | ||
| High Voltage Arc Tracking Rate (HVTR) | UL 746 | ||
| 0.710 mm | 115 | mm/min | |
| 3.05 mm | 17.5 | mm/min | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.710 mm | 45 | sec | |
| 1.47 mm | 90 | sec | |
| 3.05 mm | 120 | sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN ANC120 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Tisarbon® PC 10 GFR FR | Tisan | PC | Tisarbon® |
| NEXUS PE HDPE-862 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| Kumho KTR KTR-602 | Korea Kumho Petrochemical Co., Ltd. | SBS | Kumho KTR |
| Infino WR-7000P | LOTTE ADVANCED MATERIALS CO., LTD. | ASA+PC | Infino |