Hanwha Total PP FB76S
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | klLKxR_Hanwha-Total-PP-FB76S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FB76S is a High Specific Weight polypropylene that contains inorganic fillers in large quantities, so vibration-resistant stability is very good. Superb mechanical properties and size stability make this grade perfect for use in acoustic instruments such as a speaker housings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 to 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 19.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 3 | 2550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.794 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Front Temperature | 200 to 220 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 39.2 to 88.3 | MPa | |
| Holding Pressure | 58.8 to 98.1 | MPa | |
| Screw Speed | 30 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPH343T8 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| SABIC® PP 579S | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| SUPREME HIPS SH 3001 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Nycal™ 2050R50 | Technical Polymers, LLC | Nylon 612 | Nycal™ |
| SEQUEL® 1825 FP BLK | LyondellBasell Industries | PP, Unspecified | SEQUEL® |