AKROMID® B3 GF 15 S3 natural (2547)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | klCySU_AKROMID-B3-GF-15-S3-natural-2547-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 15 S3 natural (2547) is a 15% glass fibre reinforced, dry impact modified polyamide 6 with medium stiffness and rigidity and light inherent color. Applications are highly integrated housings in the automotive, electro and furniture industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.21 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4000 | MPa | ISO 178 |
| Flexural Stress 2 | 160 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 8.5 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 15 | % | ISO 1172 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 216 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | °C | ISO 75-2/A |
| Melting Temperature 4 | 222 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALECCA K-700 | Denka Company Limited | ABS | MALECCA |
| Texalan® 3 Series 395A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| Wellamid® MRGF25/15 42H-GY1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| NYLOY® M-0030N-V N4-1 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Elastollan® 1075 AU | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |