SABIC® LDPE HP2022N
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kkW4rs_SABIC-LDPE-HP2022N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description HP2022 series resins are Low Density Polyethylene grades suitable for general purpose packaging. They exhibit better draw down, good opticals and mechanical properties. Typical Applications Thin shrink film, lamination film, produce bags, textile packaging, soft goods packaging, general purpose bags with good optics and t-shirts carrier bags. HP2022N: No Slip & No Antiblock |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 30 µm, blown film | 160 | MPa | ASTM D882 |
| 1% secant, TD : 30 µm, blown film | 180 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 8.00 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 7.00 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 21.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 18.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 290 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 570 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 80 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 180 | g | ASTM D1922 |
| TD : 30 µm, blown film | 150 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 80 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured by producing 30 µ film with 2.5 BUR using 100% HP2022N. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 6115 HS | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA Polyamide |
| Bolv ABS | Shandong Jining Bolv Chemicals Co.,Ltd | ABS | Bolv |
| CERTENE™ LDF-0221J | Muehlstein | LDPE | CERTENE™ |
| POFEX EP8004S150F | POLYROCKS CHEMICAL CO., LTD | XLPE | POFEX |
| Sylvin 29168-90 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |