OPNYL OP66GF50
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OPNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | khQwXo_OPNYL-OP66GF50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 66 - Glass reinforced (50 %), high tensile strength, stiffness and HDT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.57 | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.35 | 0.20 to 0.35 | % | ASTM D955 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1 | 10000 | 8500 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 250 | 175 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 | 3.0 | % | ASTM D638 |
| Flexural Modulus 4 | 13000 | 10200 | MPa | ASTM D790 |
| Flexural Strength 5(Yield) | 265 | 200 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | 130 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Annealed, 3.20 mm | 254 | -- | °C | |
| 1.8 MPa, Annealed, 3.20 mm | 250 | -- | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202 TFE 15 | RTP Company | Nylon 66 | RTP |
| S&E PVC GF-1807 | S&E Specialty Polymers, LLC | PVC+NBR | S&E PVC |
| Sylvin 8692-75 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 4PROP® 9D12230 | 4Plas | PP Homopolymer | 4PROP® |
| Petrotene® PP A3 C35 BRC0001 PH333 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |