MAXAMID™ EPDMRC206-HSL-BK09
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | khCST7_MAXAMIDEPDMRC206HSLBK09.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXAMID™ EPDMRC-206-HSL is available in black only, with internal and external lubricants, UV stabilized and other modifications available. Manufactured with recycled content. Further information and details are available upon request. |
| General Information | |
|---|---|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 80 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1690 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 66.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 860 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 59.0 | °C | ASTM D648 |
| Peak Melting Temperature | 215 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.20 | % | |
| Mold Temperature | 60 - 85 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ S95 | Miracll Chemicals Co., Ltd. | TPU-Capro | Mirathane™ |
| RTP 107 UV | RTP Company | PP Homopolymer | RTP |
| SEPAZ™ LA50 | Mando Advanced Materials Co., Ltd. | Nylon 66 | SEPAZ™ |
| Celanex® 3200 | Celanese Corporation | PBT | Celanex® |
| TABOREN® PH 52 G 20-094 | SILON s.r.o. | PP Homopolymer | TABOREN® |