SABIC® PPcompound 8611
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kh6IMM_SABICPPcompound8611.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8611 is a development grade, elastomer-modified mineral filled Polypropylene for automotive exterior applications. This material has been designed to combine a good stiffness and excellent impact performance with good processing and surface esthetics. AN UV stabilised grade is available as well (8611P). SABIC® PPcompound 8611 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.985 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 32 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1500 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | ||
| Yield, injection molding | 20.0 | MPa | ISO 527-2/1A |
| Fracture, injection molding | 15.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break, Injection Molded) | 60 | % | ISO 527-2/1A |
| Flexural Modulus 1(Injection Molded) | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -20°C, injection molding | 10 | kJ/m² | ISO 180/1A |
| 0°C, injection molding | 30 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 40 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 100°C) | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | Type 1A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYRIN™ CM 3630E EL | The Dow Chemical Company | CPE | TYRIN™ |
| Celstran® PP-GF40-05 Black | Celanese Corporation | PP, Unspecified | Celstran® |
| FERREX® GPP20CS43HB-GY | Ferro Corporation | PP, Unspecified | FERREX® |
| 3M™ Dyneon™ Fluoroelastomer FC 2176Z | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Pearlthane® 15N95UV | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Pearlthane® |