LNP™ THERMOCOMP™ LF004E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kgfy0T_LNP-THERMOCOMP-LF004E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LF004E is a compound based on Polyetheretherketone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound LF-1004 EM Product reorder name: LF004E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.71 | % | |
| Across Flow : 24 hr | 1.2 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8730 | MPa | ASTM D638 |
| -- | 8620 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 147 | MPa | ASTM D638 |
| Break | 124 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.3 | % | ASTM D638 |
| Break | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 8090 | MPa | ASTM D790 |
| -- 5 | 7720 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 222 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 228 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 42 | J/m | ASTM D256 |
| 23°C 7 | 4.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 480 | J/m | ASTM D4812 |
| 23°C 8 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.14 | J | ASTM D3763 |
| -- | 1.54 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 337 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 335 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 320 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 305 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC SR3109FC | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| EMERGE™ PC 8430-15 | Trinseo | PC | EMERGE™ |
| INSPIRE™ TF1305 ESU | Trinseo | TPO | INSPIRE™ |
| Durez® 33824 | SBHPP | Phenolic | Durez® |
| Sylvin 9812-75 Red 6295 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |