RTP 3487-3
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kgcsRr_RTP-3487-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.010 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 34500 | MPa | ASTM D638 |
| Tensile Strength | 117 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 27600 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 285 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 332 - 366 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® A30N02 | Polyram Ram-On Industries | Nylon 66 | Polytron® |
| SCANAMID 6 B32^E | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Argothane® 18411 | Argotec LLC | TPU, Unspecified | Argothane® |
| CP PRYME® Polypropylene PPC100RC-35M | Chase Plastics Services Inc. | PP Random Copolymer | CP PRYME® Polypropylene |
| Karina BROWN PVC COMPOUND -E MICRO-EX 6536/212 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |