STAR-THERM® E TA 10-2C
| Category: | PPA , Polyphthalamide |
| Manufacturer: | EPIC Polymers |
| Trademark: | STAR-THERM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kgbuRn_STAR-THERM-E-TA-10-2C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STAR-THERM® E TA 10-2C is a Polyphthalamide (PPA) product filled with 20% carbon fiber. It is available in Europe. Primary characteristic: conductive. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.26 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.25 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 15200 | 14600 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 210 | 200 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 14500 | 13700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 300 | 285 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 | 30 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 300 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 285 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 2.1E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.45 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+3 | -- | ohms | IEC 60093 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 320 to 340 | °C | |
| Middle Temperature | 320 to 335 | °C | |
| Front Temperature | 320 to 335 | °C | |
| Nozzle Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | < 340 | °C | |
| Mold Temperature | 135 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP UC4X206-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 1600 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| AKROMID® A3 GF 20 1 black (2307) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Pinnacle PP 4211 | Pinnacle Polymers | PP Impact Copolymer | Pinnacle PP |
| WELLAMID Nylon 6600-PA66-GV 30 HWV0CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |