Ebalta AH 110 / TG
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kgSnxk_Ebalta-AH-110-TG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 to 88 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3050 to 3650 | MPa | ISO 178 |
| Flexural Stress | 125 to 145 | MPa | ISO 178 |
| Compressive Stress | 85.0 to 105 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 20 to 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 87 to 93 | °C | DIN 53458 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 22 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.11 to 1.15 | g/cm³ | |
| Viscosity (25°C) | 1.7 to 2.2 | Pa·s | |
| Curing Time (20°C) | 10 to 17 | hr | |
| Pot Life 1(20°C) | 35 to 40 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| apilon 52® D 30 L | API SpA | TPU-Polyester | apilon 52® |
| Iupital® TC3030 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| RONFALIN® ASA 3324 U | A. Schulman Europe | ASA | RONFALIN® |
| Kepital® F25-03H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| CYCOLAC™ EX58F resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |