Zytel® HTN 51G35HSL BK083
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kfPgx7_Zytel-HTN-51G35HSL-BK083.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12000 | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 210 | 200 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | 2.3 | % | ISO 527-2 |
| Flexural Modulus | 10500 | 10000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 9.0 | -- | kJ/m² | |
| -30°C | 10 | 9.0 | kJ/m² | |
| 23°C | 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 40 | kJ/m² | |
| 23°C | 70 | -- | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 10 | -- | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 67 | -- | kJ/m² | |
| 23°C | 65 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 284 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 264 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 5.7E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 7.2E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.00 | -- | ||
| 1 MHz | 3.80 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 9.0E-3 | -- | ||
| 1 MHz | 0.017 | -- | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 21 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.850 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 26 | -- | % | ISO 4589-2 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Odor | 4 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V903 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Precision Polymer S60H | Precision Polymer Engineering Ltd. | Silicone | Precision Polymer |
| Mowiol® 26-88 G2 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| Kingfa ABP-0520 | Kingfa | PP, Unspecified | Kingfa |
| LEXAN™ BPL1000 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |