SCHULABLEND® SCHULABLEND® M/MA 6301 U
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kebbtB_SCHULABLENDSCHULABLENDMMA6301U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC / ASA, UV stabilized, with good flow. |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 51.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 45.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.8 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 100 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 3.5% strain | 77.0 | MPa | ISO 178 |
| 5.7% strain | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 138 | °C | ISO 306/A50 |
| -- | 126 | °C | ISO 306/B50 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 70 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME GPPS SC202LV | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Andur 90 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Escorene™ Ultra UL 00226CC | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Lupoy® 1201-18 | LG Chem Ltd. | PC | Lupoy® |
| PPR POM17 | Premier Plastic Resins, Inc. | Acetal (POM) Homopolymer | PPR |