Alpha PVC GW 3040 NATURAL LCF
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | AlphaGary |
| Trademark: | Alpha PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kceP7N_Alpha-PVC-GW-3040-NATURAL-LCF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A LEAD FREE, 60°C TO 80°C TEMPERATURE RATED, FLAME RETARDED CABLE JACKETING COMPOUND. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 - 1.52 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 93 - 99 | ASTM D2240 | |
| Shaw A, 15 seconds | 89 - 95 | ASTM D2240 | |
| Shaw D | 55 - 61 | ASTM D2240 | |
| Shaw D, 15 seconds | 39 - 45 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| 0.381 mm | 17.2 | MPa | ASTM D412 |
| 0.610 mm | 15.9 | MPa | ASTM D412 |
| 1.91 mm | 14.5 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Fracture, 0.610mm | 250 | % | ASTM D412 |
| Fracture, 1.91mm | 280 | % | ASTM D412 |
| Fracture, 0.381mm | 230 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 1 | UL Unspecified | ||
| 100°C, 168 hr | 0.0 | % | UL Unspecified |
| 100°C, 240 hr | 5.0 | % | UL Unspecified |
| 113°C, 168 hr | 8.0 | % | UL Unspecified |
| Change in Ultimate Elongation in Air 2 | UL Unspecified | ||
| 100°C, 168 hr | -15 | % | UL Unspecified |
| 100°C, 240 hr | -17 | % | UL Unspecified |
| 113°C, 168 hr | -38 | % | UL Unspecified |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -15.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (23°C, 100 MHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (23°C, 100 MHz) | 0.026 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 39 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 154 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 166 | °C | |
| Cylinder Zone 4 Temp. | 171 | °C | |
| Cylinder Zone 5 Temp. | 177 | °C | |
| Adapter Temperature | 177 | °C | |
| Melt Temperature | 171 - 182 | °C | |
| Die Temperature | 177 | °C |
| Extrusion instructions |
|---|
| It may be necessary to adjust barrel temp to attain the desired melt temperatureScrew Design: Standard PVC metering screw with a 3:1 compression ratio |
| Note Message | |
|---|---|
| 1 . | Thickness: 24 mil |
| 2 . | Thickness: 24 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3582C | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tenac™-C TFC64 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Topilene® R530 | Hyosung Corporation | PP Homopolymer | Topilene® |
| Laprene® 83FM00A90 | SO.F.TER. SPA | SEBS | Laprene® |
| ExxonMobil™ HDPE HTA 002HD5 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |