Innothane® FM-110
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kcXSEB_Innothane-FM-110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM-110 is a open-cell polyurethane foam formulated for hand-batch and meter-mix dispensing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. FM-110 is particularly suited for low volume production of arm rests and seat cushions. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 0.144 to 0.192 | g/cm³ | |
| Base Resin | 1.08 | g/cm³ | |
| Hardener | 1.08 | g/cm³ |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 15 to 25 | min | |
| Cream Time | 0.8 to 1.2 | min | |
| Rise Time | 3.0 | min | |
| Tack Free Time | 3.8 to 4.3 | min |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.90 | Pa·s | |
| 25°C 2 | 1.0 | Pa·s | |
| 25°C 3 | 1.1 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILENE® P K30VA S | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| Bapolan® 6409 | Bamberger Polymers, Inc. | PS (HIPS) | Bapolan® |
| AMPLIFY™ TY 1151 | The Dow Chemical Company | MAH-g | AMPLIFY™ TY |
| Hypro® PP-RP 35/1.5C | Entec Polymers | PP Random Copolymer | Hypro® |
| Lusin® Clean OH 251 | Chem-Trend L.P. | Unspecified | Lusin® |