DENKA STYROL HRM-2S-311
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA STYROL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kbeilm_DENKA-STYROL-HRM-2S-311.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High molecular weight transparent polystyrene resins with superior impact strength |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 23°C) | 75 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | < 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3400 | MPa | ISO 178 |
| Flexural Stress 2 | 109 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.6 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 102 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 90.0 | % | ISO 13468 |
| Haze (2000 µm) | 0.30 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 2180 EM | RTP Company | PEI | RTP |
| Sindustris ABS LHI232H | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| TORZEN® T2000HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| LG SAN 90HR | LG Chem Ltd. | SAN | LG SAN |
| Panlite® AM-8030 | TEIJIN LIMITED | PC+Polyester | Panlite® |