| Infino MKD-1016 is a Polyamide product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 275°C/2.16 kg | 13 | g/10 min | |
| 300°C/1.2 kg | 10 | g/10 min | |
| Molding Shrinkage - Flow | |||
| 3.20 mm | 0.30 | % | ASTM D955 |
| 3.20 mm | 0.030 | % | ISO 2577 |
| Water Absorption | |||
| 23°C, 24 hr | 3.9 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 3.9 | % | ISO 62 |
| Ash Content | |||
| -- | 55 | % | ISO 3451 |
| -- | 55 | % | ASTM D5630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19000 | MPa | ASTM D638 |
| -- | 18600 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 260 | MPa | ASTM D638 |
| Yield | 260 | MPa | ISO 527-2/5 |
| Break 3 | 260 | MPa | ASTM D638 |
| Break | 260 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 4.2 | % | ASTM D638 |
| Break | 4.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 15000 | MPa | ASTM D790 |
| -- 6 | 16000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 330 | MPa | ASTM D790 |
| -- 8 | 330 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 17 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 130 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 120 | J/m | ASTM D256 |
| 23°C 10 | 17 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 250 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 250 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 280 to 290 | °C | |
| Front Temperature | 300 to 310 | °C | |
| Nozzle Temperature | 300 | °C | |
| Mold Temperature | 60.0 to 130 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4408 HS L | RTP Company | Nylon, Unspecified | RTP |
| STERLENE™ HMU210 | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| Sylvin 9969-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| KOPET® KP133G45BL | Kolon Plastics, Inc. | PET | KOPET® |
| Infino LM-1090 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |