Niplene C40
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niplene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kbNesQ_Niplene-C40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer, filled with 40% calcium carbonate, for the injection moulding of items of medium hardness and good aesthetical surface. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 to 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 3 | 3000 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 68.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 5 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SITRAMID CF10-M15 / C94150 | SITRAPLAS GmbH | Nylon 6 | SITRAMID |
| THERMORUN® 3855B/N | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |
| Clariant PC PC-1100G30TF15 | Clariant Corporation | PC | Clariant PC |
| ELASTOSIL® R plus 4305/50 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| OTECH ALLOY OTO8150LSZH - Riser Insulation | OTECH Corporation | TP, Unspecified | OTECH ALLOY |