| Loyblend® TA-1200 is a general purpose PC/ABS polymer alloy. This grade features good impact and chemical resistance, good low temperature ductility with ease of processability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.55 to 0.75 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2850 | MPa | ASTM D638 |
| Tensile Strength | 56.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 2250 | MPa | ASTM D790 |
| Flexural Strength | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 650 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 98.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 210 to 245 | °C | |
| Middle Temperature | 220 to 250 | °C | |
| Front Temperature | 225 to 260 | °C | |
| Nozzle Temperature | 230 to 260 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3565 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Moplen HP500N | LyondellBasell Industries | PP Homopolymer | Moplen |
| DURANEX® 551HS | Polyplastics Co., Ltd. | PBT | DURANEX® |
| EOS PA 2200 Top Speed 1.0 | EOS GmbH | Nylon 12 | EOS |
| Huafon JF-P-8705 / JF-I-8805 (outsole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |