ARLEN™ A350
| Category: | Nylon 6T , Polyamide 6T |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | ARLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kb5x2o_ARLEN-A350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ARLEN™A350 is a polyamide 6T (nylon 6T) material, which contains a 50% glass fiber reinforced material. This product is available in North America,. ARLEN™The main characteristics of A350 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.63 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow : 2.00mm | 0.20 | -- | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.60 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.20 | -- | % | ASTM D570 |
| 100°C, 24 hr | 1.2 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 300 | 270 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 3.0 | % | ASTM D638 |
| Flexural Modulus | 17000 | 15000 | MPa | ASTM D790 |
| Flexural Strength | 430 | 390 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 150 | 160 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 310 | -- | °C | ASTM D648 |
| Glass Transition Temperature | 125 | -- | °C | DSC |
| Melting Temperature | 320 | -- | °C | |
| Linear thermal expansion coefficient | ASTM D696 | |||
| Flow | 1.8E-5 | -- | cm/cm/°C | ASTM D696 |
| Lateral | 4.2E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 29 | -- | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.50 | -- | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.018 | -- | ASTM D150 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Hopper Temperature | 50.0 - 90.0 | °C | |
| Rear Temperature | 315 - 330 | °C | |
| Middle Temperature | 320 - 335 | °C | |
| Front Temperature | 325 - 340 | °C | |
| Nozzle Temperature | 325 - 340 | °C | |
| Mold Temperature | 90.0 - 140 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 150 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Medium Pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP8607A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Hostacom EP KC 10 Z 50 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Integra™ PC 5025 F1 | PolySource, LLC | PC | Integra™ PC |
| Latiohm 75/4-08 PD01 G/30 | LATI S.p.A. | PBT | Latiohm |
| Kinta FR6000 | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 6 | Kinta |