Durethan® BKV 50 H2.0 901510

Category:	Nylon 6 , Polyamide 6
Manufacturer:	LANXESS GmbH
Trademark:	Durethan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kb42XT_DurethanBKV50H20901510.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PA 6, 50 % glass fibers, injection molding, heat-aging stabilized

General Information
Filler / Reinforcement	Glass fiber reinforced material, 50% filler by weight
Additive	heat stabilizer
Features	Good heat aging resistance
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity
--	1.57	--	g/cm³	ASTM D792
23°C	1.57	--	g/cm³	ISO 1183
Apparent Density	0.70	--	g/cm³	ISO 60
Molding Shrinkage
Vertical flow direction : 280°C, 3.00mm ¹	0.85	--	%	ISO 2577
Vertical flow direction : 120°C, 2 hours, 3.00mm ²	0.050	--	%	ISO 294-4
Flow direction : 280°C, 3.00mm ³	0.16	--	%	ISO 2577
Flow direction : 120°C, 2 hours, 3.00mm ⁴	0.020	--	%	ISO 2577
Water Absorption				ISO 62
Saturated, 23°C	5.0	--	%	ISO 62
Equilibrium, 23°C, 50% RH	1.5	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	250	109	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
23°C ⁵	15000	9500	MPa	ASTM D638
23°C	16300	9800	MPa	ISO 527-2/1
Tensile Strength
Fracture, 23°C	210	150	MPa	ASTM D638
Fracture, 23°C	220	140	MPa	ISO 527-2/5
Tensile Elongation
Fracture, 23°C	2.0	4.0	%	ASTM D638
Fracture, 23°C	3.0	5.0	%	ISO 527-2/5
Tensile Creep Modulus				ISO 899-1
1 hr	--	8100	MPa	ISO 899-1
1000 hr	--	6600	MPa	ISO 899-1
Flexural Modulus
23°C	13500	7690	MPa	ASTM D790
23°C ⁶	15100	9700	MPa	ISO 178/A
Flexural Strength
23°C	350	220	MPa	ASTM D790
23°C ⁷	360	230	MPa	ISO 178
Flexural Strain at Flexural Strength ⁸(23°C)	3.0	5.0	%

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behavior ⁹(> 1.00 mm)	passed	--		ISO 3795

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 6, GHR, 14-160, GF50	--		ISO 1874

Injection	Dry	Unit	Test Method
Residual Moisture Content	0.030 - 0.12	%	Karl Fisher

Films	Dry	Conditioned	Unit	Test Method
Film Puncture Energy				ISO 6603-2
-- ¹⁰	3.70	--	J	ISO 6603-2
-- ¹¹	4.20	8.90	J	ISO 6603-2
Film Puncture Force				ISO 6603-2
-- ¹²	1060	--	N	ISO 6603-2
-- ¹³	1200	--	N	ISO 6603-2

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	15	13	kJ/m²	ISO 179/1eA
23°C	20	25	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	85	80	kJ/m²	ISO 179/1eU
23°C	100	100	kJ/m²	ISO 179/1eU
Notched Izod Impact
-40°C, 3.18 mm	130	130	J/m	ASTM D256
23°C, 3.18 mm	170	200	J/m	ASTM D256
-30°C	12	12	kJ/m²	ISO 180/1A
23°C	20	25	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength				ISO 180/1U
-30°C	80	80	kJ/m²	ISO 180/1U
23°C	85	85	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, not annealed, 3.99mm	215	--	°C	ASTM D648
0.45 MPa, not annealed	215	--	°C	ISO 75-2/B
1.8 MPa, not annealed, 3.99mm	200	--	°C	ASTM D648
1.8 MPa, not annealed	205	--	°C	ISO 75-2/A
Vicat Softening Temperature	> 200	--	°C	ISO 306/B50, ISO 306/B120
Melting Temperature ¹⁴	222	--	°C	ISO 11357-3
Linear thermal expansion coefficient				ISO 11359-2
Flow : 23 to 55°C	2.0E-5	--	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	7.0E-5	--	cm/cm/°C	ISO 11359-2
RTI Elec				UL 746
0.750 mm	65.0	--	°C	UL 746
1.50 mm	120	--	°C	UL 746
RTI Imp				UL 746
0.750 mm	65.0	--	°C	UL 746
1.50 mm	95.0	--	°C	UL 746
RTI				UL 746
0.750 mm	65.0	--	°C	UL 746
1.50 mm	140	--	°C	UL 746

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+13 - 1.0E+14	1.0E+12 - 1.0E+13	ohms	IEC 60093
Volume Resistivity (23°C)	1.0E+15 - 1.0E+16	1.0E+12 - 1.0E+13	ohms·cm	IEC 60093
Dielectric Strength				IEC 60243-1
23°C, 1.00 mm	35	26	kV/mm	IEC 60243-1
23°C, 3.00 mm	40	35	kV/mm	IEC 60243-1
Dielectric Constant				IEC 60250
23°C, 50 Hz ¹⁵	4.00	--		IEC 60250
23°C, 1 MHz ¹⁶	4.00	5.00		IEC 60250
23°C, 100 Hz	5.30	14.2		IEC 60250
23°C, 1 MHz	4.30	5.00		IEC 60250
Dissipation Factor				IEC 60250
23°C, 50 Hz	0.010	--		IEC 60250
23°C, 100 Hz	0.036	0.32		IEC 60250
23°C, 1 MHz	0.024 0.015	0.089 0.14		IEC 60250
Comparative Tracking Index
Solution a	550	--	V	IEC 60112
--	--	375	V	ASTM D3638

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
0.750 mm	HB	--		UL 94
1.50 mm	HB	--		UL 94
1.60 mm	HB	--		UL 94
3.00 mm	HB	--		UL 94
3.20 mm	HB	--		UL 94
Glow Wire Flammability Index (2.00 mm)	650	--	°C	IEC 60695-2-12
Oxygen Index ¹⁷	24	--	%	ISO 4589-2

Injection	Dry	Unit	Test Method
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 - 6.0	hr
Processing (Melt) Temp	270 - 290	°C
Mold Temperature	80.0 - 120	°C

Note Message
1 .	150x150x3; MT 80°C; 400 Bar
2 .	150x150x3
3 .	150x150x3; MT 80°C; 400 Bar
4 .	150x150x3
5 .	1.0 mm/min
6 .	2.0 mm/min
7 .	2.0 mm/min
8 .	Pull Rate: 2 mm/min; 50% RH
9 .	US-FMVSS302
10 .	-30°C
11 .	23°C
12 .	-30°C
13 .	23°C
14 .	10°C/min
15 .	Tinfoil Electrodes
16 .	Tinfoil Electrodes
17 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
Moplen EPS30R	Shazand (Arak) Petrochemical Corporation	PP Copolymer	Moplen
Network Polymers PC 1514 UV	Network Polymers, Inc.	PC	Network Polymers PC
LG ABS HI100H	LG Chem Ltd.	ABS	LG ABS
TechnoGreen PP LGF 60-10-04	TechnoCompound GmbH	PP, Unspecified	TechnoGreen
LEXAN™ FXEMPX2L resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™