Order Products : sales@su-jiao.com
Plaslube® PE 4000
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kahNfp_Plaslube-PE-4000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plaslube® PE 4000 is an Ultra High Molecular Weight Polyethylene product. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.941 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/1.05 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 2.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 66 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 32.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 80 | % | ASTM D638 |
| Flexural Modulus | 896 | MPa | ASTM D790 |
| Flexural Strength | 48.3 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.27 | ||
| vs. Steel - Static | 0.19 | ||
| Wear Factor | 120 | 10^-8 mm³/N·m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 93.3 | °C | |
| 1.8 MPa, Unannealed | 54.4 | °C | |
| CLTE - Flow | 9.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity | ASTM D3702 | ||
| 10 fpm | 3000 | psi·fpm | |
| 100 fpm | 5000 | psi·fpm | |
| 1000 fpm | 2500 | psi·fpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax PL948N | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| DOMAMID® 66G25V0AH | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Lifoflex® UVX 40.01 B038-8 | ELASTO | TPE | Lifoflex® |
| Karina COMP. PVC BRANCO -E 703D10/ 58-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUND 924D10/349-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |