INSPIRE™ DTF8000ES
| Category: | TPO , Experimental Compounded Polypropylene |
| Manufacturer: | Trinseo |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kaNd7L_INSPIRE-DTF8000ES.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INSPIRE™ TF 8000 ES is a superior scratch and mar resistant low gloss talc filled interior grade TPO exhibiting excellent low temperature ductility, high modulus and heat performance. Main Characteristics:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 24.8 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2220 | MPa | ISO 178 |
| Scratch Resistance - Instrumented | ASTM D7027-05 | ||
| -- 2 | 26 | N | |
| -- 3 | 31 | N |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Five Finger Scratch 4 | 15 | N | FLTM BN108-13 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 3.8 | kJ/m² | |
| 23°C | 28 | kJ/m² | |
| Instrumented Dart Impact 5 | ASTM D3763 | ||
| 0°C, 3.20 mm, Fully Ductile | 28.4 | J | |
| 23°C, 3.20 mm, Fully Ductile | 21.6 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 113 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 6 | 30 | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Textured |
| 3 . | Smooth |
| 4 . | GMW3383 |
| 5 . | 6.70 m/sec |
| 6 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPC PVC SM84E | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| Chemical Resources HD40948 | Chemical Resources, Inc. | HDPE | Chemical Resources |
| COSMOTHENE® EVA H2020 | TPC, The Polyolefin Company (Singapore) Pte Ltd | EVA | COSMOTHENE® EVA |
| KF 1300 | Kureha Corporation | PVDF | KF |
| PLUSTEK PD502G6 | Polyram Ram-On Industries | Nylon 12 | PLUSTEK |