LNP™ THERMOCOMP™ DX06094 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kYhsKP_LNP-THERMOCOMP-DX06094-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP DX06094 is a compound based on Polycarbonate resin containing Glass Fiber . Added features include: High Impact, Non- Brominated & Non-Chlorinated Flame Retardant and Mold Release. UL listing for BK only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.22 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8500 | MPa | ISO 178 |
| Flexural Stress 3 | ISO 178 | ||
| -- 4 | 206 | MPa | |
| -- 5 | 208 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 48 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8(1.8 MPa, Unannealed, 64.0 mm Span) | 138 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.3E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.9E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Molded |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | Break |
| 5 . | Yield |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NG15-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Chemfluor UHMW Polyethylene Flim | Saint Gobain - Norton | UHMWPE | Chemfluor |
| Grilamid® XE 4107 black 9992 | EMS-GRIVORY | Nylon 6/12 | Grilamid® |
| ENFLEX V1073A BLK UV | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
| LUVOCOM® 1-7893/GY VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |