TECACOMP® PPA TRM XS black 4173
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kXA7uZ_TECACOMPPPATRMXSblack4173.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (330°C/5.0 kg) | 50.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.47 | % | ISO 294-4 |
| Flow | 0.22 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16100 | MPa | ISO 527-2/50 |
| Tensile Stress | 200 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 289 | °C | ISO 75-2/A |
| Glass Transition Temperature | 100 - 140 | °C | DIN 53765 |
| Melting Temperature | 285 - 315 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 0.70 | W/m/K | DIN EN 821 |
| -- 2 | 1.1 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 150 | °C | |
| short term | 250 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 315 - 340 | °C | |
| Mold Temperature | 100 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michimid K4100GFMN40 | API Polymers, Inc. | Nylon 6 | Michimid |
| WELLAMID Nylon 6000/52 GV 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| EPO-TEK® TV1003-LV | Epoxy Technology Inc. | PI, TS | EPO-TEK® |
| HiFill® PC / ABS 830 GF10 | Techmer Engineered Solutions | PC | HiFill® |
| Lifoflex® UV 70 GC 1070 | ELASTO | SEBS | Lifoflex® |