DOW™ LLDPE 1613.11
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kUgW1x_DOW-LLDPE-1613-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dow LLDPE 1613.11 is a Linear Low Density Polyethylene Resin, 1-hexene copolymer, produced in the Solution process. This resin is designed to be used in blown extrusion to produce films for industrial applications and consumer packaging. It contains slip and antiblock additives. Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance | 7.66 | J/cm³ | Internal Method |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 51 µm | 189 | MPa | |
| 2% Secant, TD : 51 µm | 224 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 11.2 | MPa | |
| TD : Yield, 51 µm | 11.9 | MPa | |
| MD : Break, 51 µm | 33.5 | MPa | |
| TD : Break, 51 µm | 31.7 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 51 µm | 900 | % | |
| TD : Break, 51 µm | 890 | % | |
| Dart Drop Impact (51 µm) | 270 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 750 | g | |
| TD : 51 µm | 1100 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 42 | ASTM D2457 | |
| Haze (50.8 µm) | 22 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4560 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Celcon® GB25 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Geon™ Vinyl Rigid Molding M3000 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| LNP™ COLORCOMP™ J1000E compound | SABIC Innovative Plastics Europe | PESU | LNP™ COLORCOMP™ |
| INDURE™ X220-UV NAT | LyondellBasell Industries | Polyolefin, Unspecified | INDURE™ |