Bayblend® M750
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kTuXvT_Bayblend-M750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+ABS) blend; Vicat/B 120 temperature = 126°C; meet certain requirements of ISO Standard 10993-1. For further information please contact Covestro. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.12 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 260°C, 2.00 mm | 0.70 to 0.90 | % | |
| Flow : 260°C, 2.00 mm | 0.70 to 0.90 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.60 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 47.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.8 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 127 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 104 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 126 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 8.5E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.00 | ||
| 23°C, 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 2.5E-3 | ||
| 23°C, 1 MHz | 0.011 | ||
| Comparative Tracking Index (Solution A) | 325 | V | IEC 60112 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 2(260°C) | 265 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 60x60x2 mm, 80°C MT, 500 bar |
| 2 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-50MK(S) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Bormed™ SC876CF | Borealis AG | PP Random Copolymer | Bormed™ |
| Grilamid® TR XE 4139 black 9231 | EMS-GRIVORY | Nylon, Unspecified | Grilamid® |
| HiFill® PA6 GM40 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| ICORENE® N6603 | ICO Polymers EMEA, A Division of A. Schulman | ABS | ICORENE® |