| Category: | PC , Polycarbonate |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | NAXELL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kTttzk_NAXELL-PCR210HFIM-BK200.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| Further information and details are available upon request. |
| General Information | |
|---|---|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, 3.20 mm) | 60.0 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm) | 2340 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm) | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 125 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 132 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMSTER PF300J50 | Polyram Ram-On Industries | PBT | RAMSTER |
| HIVAL® 506060 NT | Nexeo Solutions, LLC. | HDPE | HIVAL® |
| INSPIRE™ TF1500 ESU | Trinseo | TPO | INSPIRE™ |
| Osterlene® PPC10-2.1 | Osterman & Company | PP Impact Copolymer | Osterlene® |
| Braskem PE LDF2023S1 | Braskem IDESA | LDPE | Braskem PE |