TECHNYL® A 218G V30 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kRRiGr_TECHNYL-A-218G-V30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide PA66, reinforced with 30% of glass fibre, for injection moulding specially stabilized to improve its resistance automotive cooling liquids. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.80 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.620 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 190 | 135 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.0 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | 9300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 12 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ||||
| -- | 80 | 95 | kJ/m² | ISO 179/1eU |
| -- 1 | 70 | -- | kJ/m² | ISO 179/1fU |
| Notched Izod Impact Strength | 11 | 16 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 5.0E+14 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 450 | 425 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index (1.60 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | After ageing in water/glycol for 200 hr at 120°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XENOY™ X5230 resin | SABIC Innovative Plastics Europe | PC+PET | XENOY™ |
| Akulon® Ultraflow K-FKMV5 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| Edgetek™ PC-20GF/000 NH FRV0 BLACK | PolyOne Corporation | PC | Edgetek™ |
| Karina WHITE PVC COMPOUND 601D10/ 1-A | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SD POLYCA™ SI6001W | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |