RTP 299 A X 108950 C
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kQhryP_RTP-299-A-X-108950-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Gravity Compound |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 4.00 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 1.0 | % | ASTM D955 |
| Moisture Content | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7580 | MPa | ASTM D638 |
| Tensile Strength | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 270 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 243 - 279 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCHPTL20 | Rainmaker Polymers LLC | PP Homopolymer | Rainmaker Polypropylene |
| Unichem 7003 | Colorite Polymers | PVC, Unspecified | Unichem |
| Formolene® 3312E | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| Later 4 G/30-V0CT2 | LATI S.p.A. | PBT | Later |
| IROGRAN® A 70 H 4714 M | Huntsman Corporation | TPU-Polyester | IROGRAN® |