RAMTAL PMH2022
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMTAL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kQdWor_RAMTAL-PMH2022.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GENERAL PURPOSE POLYACETAL HOMOPOLYMER FOR INJECTION MOLDING APPLICATION,MFI 22. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.8 to 2.2 | % | |
| -- | 1.8 to 2.2 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | |||
| Yield | 74.0 | MPa | ASTM D638 |
| Yield | 75.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 35 | % | ASTM D638, ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 165 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 165 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 175 to 200 | °C | |
| Middle Temperature | 180 to 205 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Mold Temperature | 60.0 to 110 | °C | |
| Injection Pressure | 70.0 to 105 | MPa | |
| Holding Pressure | 35.0 to 85.0 | MPa | |
| Back Pressure | 0.350 to 0.700 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperLite® SL551800-100 (10.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Vyncolit® G525M | Vyncolit N.V. | Phenolic | Vyncolit® |
| VAMPLUB PPS NEAT RESIN | Vamp Tech | PPS | VAMPLUB |
| HiFill® HDPE 1000 | Techmer Engineered Solutions | HDPE | HiFill® |
| LNP™ LUBRICOMP™ REL22 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |