Elastoflex® Bio 28110 R/T

Category:	PUR-MDI , Polyurethane (MDI)
Manufacturer:	BASF Corporation
Trademark:	Elastoflex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kPYWmN_ElastoflexBio28110RT.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
MDI flexible foam system with bio-based content designed for interior foam applications

General Information
Features	Updatable resources Good flexibility
Uses	Foam Application in Automobile Field Car interior parts

Physical	Nominal Value	Unit	Test Method
Density	0.0560	g/cm³	ASTM D3574A
Biobased Content	5.0	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	0.219	MPa	ASTM D3574E
Tensile Elongation (Break)	100	%	ASTM D3574E

Elastomers	Nominal Value	Unit	Test Method
Tear Strength ¹(10.0 mm)	0.708	kN/m	ASTM D624
Compression Set	16	%	ASTM D3574D

Flammability	Nominal Value	Unit	Test Method
Burning Rate	52	mm/min	FMVSS 302

Additional Information
Specific Gravity, Resin at 25°C: 1.02 g/cm³ Specific Gravity, Isocyanate at 25°C: 1.10 g/cm³ Viscosity, Resin at 25°C: 1460 cP Viscosity, Isocyanate at 25°C: 136 mPa-s Mix ratio at 100 index (by mass): 100 Resin, 84.6 Isocyanate Processing Data: Chemical temperature: 21 to 32°C Mold temperature: 40 to 60°C Demold time: 1 to 4 min Molded density: 48 to 72 kg/m³ Hand Mix Reactivity: Top of cup: 27 sec String gel: 39 sec End of Rise: 48 sec Free rise density: 41 kg/m³

Additional Information

Specific Gravity, Resin at 25°C: 1.02 g/cm³ Specific Gravity, Isocyanate at 25°C: 1.10 g/cm³ Viscosity, Resin at 25°C: 1460 cP Viscosity, Isocyanate at 25°C: 136 mPa-s Mix ratio at 100 index (by mass): 100 Resin, 84.6 Isocyanate Processing Data: Chemical temperature: 21 to 32°C Mold temperature: 40 to 60°C Demold time: 1 to 4 min Molded density: 48 to 72 kg/m³ Hand Mix Reactivity: Top of cup: 27 sec String gel: 39 sec End of Rise: 48 sec Free rise density: 41 kg/m³

Note Message
1 .	C mould

Resin Grade	Manufacturer	Category	Trademark
Pro-Comp™ PPBGF30-E	Southland Polymers	PP Impact Copolymer	Pro-Comp™
Spartech Polycom SC5-3210	Spartech Polycom	PP Homopolymer	Spartech
NYLOY® M-0030N-V	Nytex Composites Co., Ltd.	Nylon 66	NYLOY®
Escorene™ Ultra UL 7510	ExxonMobil Chemical	EVA	Escorene™ Ultra
THERMOLAST® K TC7HFZ (Series: UV/HF/SF)	KRAIBURG TPE	TPE	THERMOLAST® K