TEREZ PC 1007 GF 20
| Category: | PC , Polycarbonate |
| Manufacturer: | TER HELL PLASTIC GMBH |
| Trademark: | TEREZ PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kMr3lF_TEREZ-PC-1007-GF-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polycarbonate, 20% glassfiber reinforced with release agent. Medium to high flowability. Suitable for manufacturing of stiffer, thinwalled injection moulding parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 29 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melthene® -M M5321 | TOSOH Corporation | Polyolefin, Unspecified | Melthene® -M |
| API PS 550 | American Polymers, Inc. | PS (HIPS) | API PS |
| ENGAGE™ 8440 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| ESPOLEX 903 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| Hostalen PP HF500B | LyondellBasell Industries | PP Homopolymer | Hostalen |