Lupoy® SC1004AU
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kMqmpP_Lupoy-SC1004AU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Impact, High Flow, Good Weatherability Application Electric & Electronic Housing |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 54.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 130 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2110 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 89.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 5 | ASTM D256 | ||
| -30°C | 290 | J/m | |
| 23°C | 590 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 125 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.700 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Minimum Moisture Content | 0.020 | % | |
| Rear Temperature | 275 to 290 | °C | |
| Middle Temperature | 280 to 295 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Nozzle Temperature | 285 to 300 | °C | |
| Processing (Melt) Temp | 285 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| 5 . | 3.2 mm Notch Depth |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 81-403 | Colorite Polymers | PVC, Unspecified | Unichem |
| Altuglas® BS 572 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Hysun® 678 | Ravago Manufacturing Americas, LLC | ASA | Hysun® |
| Formolene® 3310Z | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| Osterlene® LLSH0917SAH | Osterman & Company | LLDPE | Osterlene® |