STYRON™ 666H
| Category: | PS (GPPS) , General Purpose Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kMkrZ4_STYRON-666H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON™ 666H is a general purpose polystyrene with easy flow and good clarity. It is recommended for applications where a specific balance of flow and strength are important. Applications:
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| Compression Molded | 3200 | MPa | |
| Injection Molded | 3300 | MPa | |
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 40.0 | MPa | |
| Yield, Injection Molded | 47.6 | MPa | |
| Ultimate, Compression Molded | 40.0 | MPa | |
| Ultimate, Injection Molded | 47.6 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, Compression Molded | 1.0 | % | |
| Break, Injection Molded | 2.0 | % | |
| Flexural Modulus | ASTM D790 | ||
| Compression Molded | 3100 | MPa | |
| Injection Molded | 3240 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Compression Molded | 56.5 | MPa | |
| Injection Molded | 89.6 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, Compression Molded | 11 | J/m | |
| 23°C, Injection Molded | 16 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 76.1 | °C | |
| 1.8 MPa, Annealed | 93.9 | °C | |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 |
| CLTE - Flow | 7.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1(1.47 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1500-55D TFE 15 | RTP Company | TEEE | RTP |
| RAMLLOY PA917G6 | Polyram Ram-On Industries | Nylon 66+PP | RAMLLOY |
| SITRAROY 2015 / C94150 | SITRAPLAS GmbH | ASA+PC | SITRAROY |
| Nycal™ 2134R33H Bk-1 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| Karina BLACK PVC COMPOUND TR-771D48/ 1-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |