LNP™ LUBRICOMP™ DL003 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kIgehU_LNPLUBRICOMPDL003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DL003 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DL-4030 Product reorder name: DL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.80 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.88 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.83 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.12 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 51.7 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2 |
| Fracture | 47.6 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.1 | % | ASTM D638 |
| Yield | 5.5 | % | ISO 527-2 |
| Fracture | 38 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 2190 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 80.3 | MPa | ASTM D790 |
| -- | 84.1 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.18 | ASTM D3702 Modified | |
| With Self-Static | 0.070 | ASTM D3702 Modified | |
| Wear Factor - Washer | 60.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D256 |
| 23°C 2 | 29 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812 | |
| 23°C 3 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 30.6 | J | ASTM D3763 |
| -- | 34.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 128 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 131 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8005-90 | Colorite Polymers | PVC, Unspecified | Unichem |
| Bamtac BPP235A | Ningbo Bamtac New Material Col, Ltd. | PP, Unspecified | Bamtac |
| Akulon® F136-E2 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| LUVOCOM® 1105-7920/RD VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Silastic® Q7-7850 | Dow Corning Corporation | Silicone | Silastic® |