SABIC® PPcompound 17T1022
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kIKng1_SABIC-PPcompound-17T1022.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 17T1022 is a 22% talc filled grade which is high heat stabilized, developed for under the bonnet applications. This material has been designed to combine a good performance profile with good processing. SABIC® PPcompound 17T1022 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.2 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1/5 | ||
| Yield, 4.00 mm, Injection Molded | 31.0 | MPa | |
| Break, 4.00 mm, Injection Molded | 25.0 | MPa | |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 13 | % | ISO 527-2/1/5 |
| Flexural Modulus 1 | 2650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 2.9 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C, Injection Molded) | 2.1 | kJ/m² | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 121 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 154 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 4080 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Colorite CS Series CS1539GP | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Diakon® LG703 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Karina CLEAR PVC COMPOUND 60/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina PVC COMPOUND GRAY E-700N18/724-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |