RTP 3887
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kHALUY_RTP-3887.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.050 to 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 35900 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 262 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 22100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 372 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 316 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 30 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 357 to 399 | °C | |
| Middle Temperature | 366 to 418 | °C | |
| Front Temperature | 385 to 427 | °C | |
| Mold Temperature | 149 to 218 | °C | |
| Injection Pressure | 68.9 to 124 | MPa | |
| Back Pressure | 0.172 to 0.689 | MPa | |
| Screw Speed | 60 to 90 | rpm | |
| Clamp Tonnage | 6.9 to 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR H6 T/05 H XF V0 NATURAL 70 | PolyOne Corporation | PP Homopolymer | Maxxam™ FR |
| RTP 149 HI | RTP Company | PP, Unspecified | RTP |
| SOLPLAST TC 2000A | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| LAPEROS® A150F | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| Hostaform® C 13021 LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |